Produced using a wide variety of material combinations such as thermoplastic polyurethane, nitrile rubber and elastic fabrics and featuring varied surface constructions from smooth to structured.
Easy and fast finger jointing system without using any glue, this range provides excellent dimension stability and is highly suitable for small pulley diameters. Our PolySprint™ belts are suitable for high speed and use the unique Nitta NBR rubber with fine textured surfaces.
Our PolySprint™ range of belts is ideal for feeding, folding and packaging and are installed in printing (web) folders, print finishing applications, packaging machines, live roller and textile applications.
| BELT TYPE | TOP SURFACE |
BOTTOM SURFACE | SURFACE MATERIAL | MAIN APPLICATIONS | THICKNESS[MM] | SPECIFIC TENSION (AT 2 % ELONGATION) [N/MM WIDTH] | MINIMUM PULLEY DIAMETER[MM] |
|---|---|---|---|---|---|---|---|
| TA09 |  |
 |
TPU/TPU | Mail sorter, bank note insertion conveyor | 0.9 | 0.5 (at 5 % elongation) |
20 |
| TA12 | |
|
TPU/TPU | Mail sorter, packaging | 1.2 | 0.7 (at 5 % elongation) |
25 |
| TA-S6 | |
 |
TPU/TPU | Mail sorter | 0.9 | 0.7 (at 5 % elongation) |
25 |
| NTA |  |
|
Knit/TPU | Mail sorter, packaging | 1.0 | 0.5 (at 5 % elongation) |
25 |
| TC |  |
|
TPU/TPU | Mail sorter | 1.4 | 0.8 (at 5 % elongation) |
40 |
| HTA09 | |
|
Hard TPU/TPU | Mail sorter, bookbinding | 0.9 | 0.5 (at 5 % elongation) |
25 |
| STC-10 | |
 |
Knit/TPU | Stacker | 1.35 | 0.5 (at 5 % elongation) |
25 |
| GTD |  |
 |
NBR/TPU | Postal, Paper | 1.45 | 1.1 (at 5 % elongation) |
25 |
| SNTC-RB22A |  |
 |
Soft TPU (Longitudal Groove)/Knit | Inclined, Declined Conveyor | 2.25 | 0.8 (at 5 % elongation) |
25 |
| SNTC-TW18A |  |
|
Soft TPU (Mini Rough Top)/Knit | Inclined, Declined Transport | 1.8 | 0.65 (at 5% elongation) |
20 |
| BELT TYPE | TOP SURFACE |
BOTTOM SURFACE | SURFACE MATERIAL | MAIN APPLICATIONS | THICKNESS[MM] | SPECIFIC TENSION (AT 2 % ELONGATION) [N/MM WIDTH] | MINIMUM PULLEY DIAMETER[MM] |
|---|---|---|---|---|---|---|---|
| DB-4E14 | |
|
TPU/TPU | Mail sorter | 1.4 | 4 (at 1 % elongation) |
25 |
| FZ-5E12 | |
|
Coated NBR/NBR | Printing/bookbinding | 1.25 | 5 (at 1 % elongation) |
35 |
| LA-4E14 |  |
|
NBR/NBR | Printing/bookbinding Roller conveyor | 1.4 | 4 (at 1 % elongation) |
25 |
| NB-2E10 |  |
 |
TPU/Knit | Sheeter | 1.0 | 2 (at 1 % elongation) |
20 |
| NB-2E10 | |
|
TPU/Knit | Sheeter | 1.4 | 2 (at 1 % elongation) |
20 |
| RT-22E70-2 |  |
 |
NBR/Fabric | Conveying corrugated board, Flexo folder gluer | 7.0 | 10 (at 0.5 % elongation) |
20 |
| TFL-15E20 |  |
|
NBR/NBR | Roller conveyor, Textile | 2.0 | 15.0 (at 1% elongation) |
40 |
| TFL-15E25 | |
|
NBR/NBR | Textile | 2.5 | 15.0 (at 1% elongation) |
25 |
| TFL-22E26-2 | |
|
NBR/NBR | Ring Spinning, OE, TFO | 2.6 | 22.0 (at 1% elongation) |
50 |
| TFL-22E26C-2 | |
 |
NBR/NBR | Covering machine | 2.6 | 22.0 (at 1% elongation) |
50 |
| TLA-30E30-2 |  |
|
NBR/NBR | DTY | 3.0 | 30.0 (at 1% elongation) |
70 |
| TTF-4E10 |  |
|
Fabric/Fabric | Bookbinding | 1.0 | 4 (at 1 % elongation) |
15 |
| TTP-8E18N |  |
 |
Fabric/Fabric | Printing & Book Binding | 1.8 | 8.0 (at 1% elongation) |
40 |
| TTZ-4E10LF |  |
 |
Fabric/NBR coated fabric | Printing & Book Binding | 1.0 | 4.0 (at 1% elongation) |
30 |
| XH-8E30 | |
|
NBR/NBR | Folder Gluer; Paper Manufacturing | 3.0 | 8.0 (at 1% elongation) |
40 |
| XH-8E40 | |
|
NBR/NBR | Folder Gluer; Paper Manufacturing | 4.0 | 8.0 (at 1% elongation) |
50 |
| XH-8E55 | |
|
NBR/NBR | Folder Gluer; Paper Manufacturing | 5.5 | 8.0 (at 1% elongation) |
80 |
| XHTG-15E34 | |
 |
NBR/Fabric | Cardboard Conveyor; Table Supported Conveyor | 3.4 | 7.5 (at 0.5% elongation) |
50 |